| TYPICAL PROPERTIES OF Torlon® 7130 |
|
| |
|
Typical
Values(1) |
|
|
|
| |
Test |
U.S.
Customary Units |
SI
Units |
|
|
|
| Property |
Method(2) |
|
Value |
Units |
|
Value |
Units |
|
| Mechanical |
|
| Tensile strength |
|
|
| -321°F (-196°C) |
D 1708 |
|
22.8 |
kpsi |
|
158 |
MPa |
| 73°F (23°C) |
D 1708 |
|
29.4 |
kpsi |
|
203 |
MPa |
| 275°F (135°C) |
D 1708 |
|
22.8 |
kpsi |
|
158 |
MPa |
| 450°F (232°C) |
D 1708 |
|
15.7 |
kpsi |
|
108 |
MPa |
| Tensile elongation |
|
|
| -321°F (-196°C) |
D 1708 |
|
3 |
% |
|
3 |
% |
| 73°F (23°C) |
D 1708 |
|
6 |
% |
|
6 |
% |
| 275°F (135°C) |
D 1708 |
|
14 |
% |
|
14 |
% |
| 450°F (232°C) |
D 1708 |
|
11 |
% |
|
11 |
% |
| Tensile modulus |
D 1708 |
|
3220 |
kpsi |
|
22.3 |
GPa |
| Flexural strength |
|
|
| -321°F (-196°C) |
D 790 |
|
45.0 |
kpsi |
|
315 |
MPa |
| 73°F (23°C) |
D 790 |
|
50.7 |
kpsi |
|
355 |
MPa |
| 275°F (135°C) |
D 790 |
|
37.6 |
kpsi |
|
263 |
MPa |
| 450°F (232°C) |
D 790 |
|
25.2 |
kpsi |
|
177 |
MPa |
| Flexural modulus |
|
|
| -321°F (-196°C) |
D 790 |
|
3570 |
kpsi |
|
24.6 |
GPa |
| 73°F (23°C) |
D 790 |
|
2880 |
kpsi |
|
19.9 |
GPa |
| 275°F (135°C) |
D 790 |
|
2720 |
kpsi |
|
18.8 |
GPa |
| 450°F (232°C) |
D 790 |
|
2280 |
kpsi |
|
15.7 |
GPa |
| Izod impact strength |
|
|
| Notched |
D 256 |
|
0.9 |
ft-lb/in |
|
47 |
J/m |
| Unnotched |
D 256 |
|
6.4 |
ft-lb/in |
|
340 |
J/m |
| Shear strength |
D 732 |
|
17.3 |
kpsi |
|
120 |
MPa |
| Compressive strength |
D 695 |
|
36.9 |
kpsi |
|
250 |
MPa |
| Compressive modulus |
D 695 |
|
1430 |
kpsi |
|
9.9 |
GPa |
| Poisson's ratio |
|
|
0.39 |
|
|
0.39 |
|
|
| Thermal |
|
| Heat deflection temperature |
|
|
| at 264 psi (1.82 MPa) |
D 648 |
|
540 |
°F |
|
282 |
°C |
| Flammability Rating(3) |
UL-94 |
|
94 V-0 |
|
|
94 V-0 |
|
| Coefficient of thermal expansion |
D 696 |
|
5 |
10-6 in/in/°F |
|
9.0 |
10-6 m/m/°C |
| Thermal conductivity |
C 177 |
|
3.6 |
Btu-in/hrft2°F |
|
0.53 |
W/mK |
| Oxygen index |
D 2863 |
|
52 |
% |
|
52 |
% |
|
| General |
|
| Moisture absorption |
D 570 |
|
0.26 |
% |
|
0.26 |
% |
| Rockwell hardness |
D 785 |
|
94 |
|
|
94 |
|
| Density |
D 1505 |
|
0.054 |
lb/in3 |
|
1.48 |
g/cm3 |
|
| |
| 1Actual properties of individual batches will vary within specification limits. |
| 2Test methods are ASTM unless otherwise noted. |
| 3These flammability ratings are not intended to reflect hazards presented by these or any other material under acutal fire conditions. |
|